VGlove nitrile examination gloves

Our VGlove nitrile examination gloves is designed for all kind of tasks that require speed and maximum protection, with its low-friction special treated inner surface. With the unique surface treatment, which combines both specialized coating and highly effective finishing, the interaction creates a smooth surface that prevents any stress to the skin despite repeated donning. The increased durability of nitrile gloves can survive rough surfaces and provides protection against typical hazards.
Manufacturer: Vglove
Please login to see the price.
  • Protection from unwanted and dangerous substances
  • Beaded cuff ensures easy donning and prevent roll down
  • Superior strength with better puncture resistance
  • Full textured or Finger Tip textured enhances wet and dry grip
  • Thinner gauge improves tactile sensitivity
  • Custom design enhances comfort and fit
  • Provide an alternative solution for individuals who are allergic to natural rubber latex

Product Specifications

MaterialSynthetic Nitrile latex.
TypeNon-Sterile Powder-Free.Ambidextrous; Finger Tip Textured; Beaded Cuff; White or Coloured (Blue, Light Blue, …)
Quality StandardsConforms to ASTM D6319Manufactured under ISO9001: 2008, ISO 13485:2003. ISO 22000:2005 Quality Management System.Manufactured from 100% nitrile (Acrylonitrile-Butadiene)
Gloves SizeExtra-small, Small, Medium, Large, Extra-large.Marked in the check box on the shipping carton with black ink.
StorageStore in a dry and cool place, the temperature not higher than 38°C.
Shelf-fife3 years from the date of manufacturing.

PHYSICAL DIMENSIONS 

DIMENSIONSStandards
VRG KHAI HOANASTM D6319
Length (mm)230 min220 min (XS, S)230 min (M, L, XL)
Width (mm)75 ± 5 (XS)85 ± 5 (S)95 ± 5 (M)105 ± 5 (L)115 ± 5 (XL)70 ± 10 (XS)80 ± 10 (S)95 ± 10 (M)110 ± 10 (L)120 ± 10 (XL)
Thickness-Single wall (mm)Fingers  : 0. 08 mm minPalm  :   0.06 mm minFingers   : 0.050 mm minPalm       : 0.05 mm min

PHYSICAL PROPERTIES AND BIOCOMPATIBILITY

TensileTensile strength (MPA)Before aging: 18Mpa minAfter aging: 20Mpa min Elongation at break (%)Before aging: 600% minAfter aging: 500% minTensile strength (MPA)Before aging: 14Mpa minAfter aging: 14Mpa min Elongation at break (%)Before aging: 500% minAfter aging: 400% min
Powder Content2 mg/glove maximum
Protein ContentFree Protein